Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | 内部方法 | 1.50 g/cm³ |
| Shrinkage rate | | 内部方法 | 0.35 % |
| Shrinkage rate | | 内部方法 | 0.80 % |
| Water absorption rate | | ISO 62 | 0.010 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-2 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | 内部方法 | 135 MPa |
| tensile strength | | 内部方法 | 95.0 MPa |
| elongation | Break | 内部方法 | 1.5 % |
| Flexural modulus | | 内部方法 | 4500 MPa |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| MeltViscosity | | ISO 11443 | 650 Pa·s |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 5E+16 ohms |
| Volume resistivity | | IEC 60093 | 2E+15 ohms·cm |
| dielectric strength | | IEC 60243-1 | 18 kV/mm |
| dielectric constant | | IEC 60250 | 3.90 |
| dielectric constant | | IEC 60250 | 3.90 |
| Dissipation Factor | | IEC 60250 | 3E-03 |
| Dissipation Factor | | IEC 60250 | 4E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | 内部方法 | 180 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 5E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 8E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.