POM BS130 SHANGHAI LANXING

Form：Granules | Grade：Enhanced level

Properties:

High mobilityMedium to high liquidity

Typical Applications:

Automotive sectorbuilding materialsIndustrial applicationsPipe fittingsEngine partsbearingValve componentsswitchPhone case

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive sector \| building materials \| Industrial applications \| Pipe fittings \| Engine parts \| bearing \| Valve components \| switch \| Phone case
Properties:	High mobility \| Medium to high liquidity

Certificates

No Data...

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			中流动性
purpose			电子、汽车、建材、轻工等工业及民生用扣具、按扣.卷轴.齿轮.轴承、滑块、阀门、键盘、开关和把手等零件。
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Elongation at Break		ASTM D638/ISO 527	34	%
Tensile modulus		ASTM D638/ISO 527	2450	kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	62	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	87	kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638	55	%
Rockwell hardness		ASTM D785	80	M
Impact strength of cantilever beam gap	凹侧23℃ 50%RH	ASTM D256	6	Kgf.cm/cm
tensile strength		ASTM D638	620	Kgf/cm
bending strength		ASTM D790	950	Kgf/cm
Bending modulus		ASTM D790	26000	Kgf/cm
compressive strength	10%变形	ASTM D695	1100	Kgf/cm
compressive strength	compressive strength	1%变形	ASTM D695	320	Kgf/cm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	18.6kg/cm	ASTM D648	110	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate		ASTM D955	1.8-2.2	%
Water absorption rate	23℃,24hrs	ASTM D570	0.22	%
melt mass-flow rate		ASTM D1238	13	g/10min
Shrinkage rate			1.8-2.2	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.