'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PA66 90G50 ASAHI JAPAN
87
Form：Granules | Grade：Injection grade
Properties:
Good appearanceHigh rigidityGlass fiber reinforcedenhance
Typical Applications:
furniture
Product Description
Certificates(1)
Datasheet
Product Description
| Typical Applications: | furniture |
| Properties: | Good appearance | High rigidity | Glass fiber reinforced | enhance |
Certificates
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 88 | kJ/m² | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 0.75mm | UL 94 | HB | |
| Basic Performance | Test Condition | Test Method | Test Result | Test Unit |
| Water absorption rate | 湿 | 1.1 | % | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| bending strength | 23°C | ISO 178 | 355 | Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 18000 | Mpa |
| Impact strength of cantilever beam gap | 干(湿) | ASTM D-256 | 127(133) | J/m |
| flexural coefficient | 干(湿) | ASTM D-790 | 15.5(12.1) | GPa |
| Rockwell hardness | 干(湿) | ASTM D-785 | 120(-) | R scale |
| 干(湿) | ASTM D-785 | 90(-) | M Scale | |
| bending strength | 干(湿) | ASTM D-790 | 373(304) | Mpa |
| tensile strength | 干(湿) | ASTM D-638 | 235(196) | Mpa |
| Elongation at Break | 干(湿) | ASTM D-638 | 2.5(3) | % |
| bending strength | ASTM D790 | 373 | Mpa | |
| Bending modulus | 23°C | ISO 178 | 14200 | Mpa |
| ASTM D790 | 15500 | Mpa | ||
| Tensile strain | Break,23°C | ISO 527-2 | 2.0 | % |
| elongation | Break | ASTM D638 | 2.5 | % |
| tensile strength | Break,23°C | ISO 527-2 | 250 | Mpa |
| ASTM D638 | 235 | Mpa | ||
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Linear coefficient of thermal expansion | 干 | ASTM D-696 | 2 | |
| Hot deformation temperature | 1.82MPa,干 | ASTM D-648 | 225 | °C |
| 0.45MPa,Unannealed | ISO 75-2/B | 240 | °C | |
| 1.8MPa,Unannealed | ASTM D648 | 225 | °C | |
| 1.8MPa,Unannealed | ISO 75-2/A | 225 | °C | |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 2E-05 | cm/cm/°C |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Shrinkage rate | 干 | 旭化成方法 | 0.2/0.5 | % |
| TD | Internal Method | 0.50 | % | |
| MD | Internal Method | 0.20 | % | |
| 吸水率(Saturation,23°C) | Internal Method | -- | % | |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO 62 | -- | % |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | M-Sale | ISO 2039-2 | 100 | |
| R-Sale | ISO 2039-2 | 120 | ||
| R-Sale | ASTM D785 | 120 | ||
| M-Sale | ASTM D785 | 90 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.