Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.38 g/cm³ |
| Water absorption rate | | ISO 62 | 0.25 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | DIN 53505 | 84 |
| ball-indentation hardness | | ISO 2039-1 | 170 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 3000 MPa |
| tensile strength | Yield | ISO 527-2 | 85.0 MPa |
| Tensile strain | Break | ISO 527-2 | 15 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 3.5 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+16 ohms |
| Volume resistivity | | IEC 60093 | 1E+20 ohms·cm |
| dielectric strength | | IEC 60243-1 | 20 kV/mm |
| dielectric constant | | IEC 60250 | 3.40 |
| Dissipation Factor | | IEC 60250 | 1E-03 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| specific heat | | DIN 52612 | 1100 J/kg/°C |
| thermal conductivity | | DIN 52612 | 0.28 W/m/K |
| Usage temperature | | | -20-115 °C |
| Usage temperature | | | <180 °C |
| Heat distortion temperature | | ISO 75-2/A | 80.0 °C |
| melting temperature | | ISO 11357 | 255 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare