Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.04 g/cm³ |
| density | | ISO 1183 | 1.04 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 22 g/10min |
| Shrinkage rate | | 内部方法 | 0.40-0.60 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 111 |
| Rockwell hardness | | ISO 2039-2 | 111 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 250 J/m |
| Charpy Notched Impact Strength | | ISO 179 | 20 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 43.0 Mpa |
| tensile strength | | ISO 527-2 | 48.0 Mpa |
| elongation | | ASTM D638 | 20 % |
| Tensile strain | | ISO 527-2 | 33 % |
| Flexural modulus | | ASTM D790 | 2350 Mpa |
| Flexural modulus | | ISO 178 | 2330 Mpa |
| bending strength | | ASTM D790 | 71.0 Mpa |
| bending strength | | ISO 178 | 72.0 Mpa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 84.0 °C |
| Heat distortion temperature | | ISO 75-2/A | 83.0 °C |
| vicat | | | 90.0to95.0 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 7.1E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.