ABS PA-757 TAIWAN CHIMEI

1728

Form：Granules | Grade：High gloss level

Properties:

High glossHigh rigidityMedium impact resistance

Typical Applications:

Automotive sectorHome appliance components

Supplier(1)

Product Description

Certificates(12)

Datasheet

Alternative Model(26)

Product Description

Typical Applications:	Automotive sector \| Home appliance components
Properties:	High gloss \| High rigidity \| Medium impact resistance

Certificates

RoHS

MSDS

RoHS

TDS

MSDS

RoHS

SVHC

Processing

Statement

Technical Data Sheet

machinability	Test Condition	Test Method	Test Result	Test Unit
Processing temperature			190-230	°C
Processing temperature	Processing temperature			180-230°C	°C
Screw speed			-	rpm
Processing temperature			180-220	°C
Dry conditions			80°C下烘料约2-3小时
Mold temperature			30-70°C	°C
Melt Temperature			-	°C
pressure			-	Mpa
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Elongation at Break		ASTM D638/ISO 527	-	%
Impact strength of cantilever beam gap		ASTM D256/ISO 179	20(3.7)	kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256/ISO 179	-	kg·cm/cm(J/M)ft·lb/in
Charpy Notched Impact Strength		ASTM D256/ISO 179	-	kg·cm/cm(J/M)ft·lb/in
bending strength		ASTM D790/ISO 178	790(11.660)	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	27000(38000)	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	R-116
elongation		ASTM D638/ISO 527	20	%
tensile strength		ASTM D638/ISO 527	490(6.950)	kg/cm²(MPa)[Lb/in²]
Tensile modulus		ASTM D638/ISO 527	-	kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	-	%
Impact strength of cantilever beam gap		ASTM D256/ISO 179	17(3.1)	kg·cm/cm(J/M)ft·lb/in
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	-	mm/mm.℃
Vicat softening temperature		ASTM D1525/ISO R306	105(221)	℃（℉）
Hot deformation temperature	HDT	ASTM D648/ISO 75	88(190)	℃（℉）
Hot deformation temperature	Hot deformation temperature	HDT	ASTM D648/ISO 75	99(210)	℃（℉）
Combustibility (rate)		UL 94	1.6mmHB
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate		ASTM D1238/ISO 1133	23	g/10min
melt mass-flow rate	melt mass-flow rate		ASTM D1238/ISO 1133	1.6	g/10min
Water absorption rate		ASTM D570/ISO 62	-	%
Shrinkage rate		ASTM D955	-	%
density		ASTM D792/ISO 1183	1.05

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.