Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D-792 | 无水｜1.5 |
| density | | ASTM D-792 | 1.9%水｜- |
| Taber abraser | | ASTM D-1044 | 无水｜30 mg/1000次 |
| Taber abraser | | ASTM D-1044 | 1.9%水｜- mg/1000次 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ASTM D-570 | 无水｜0.9 % |
| Water absorption rate | | ASTM D-570 | 1.9%水｜- % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D-256 | 1.9%水｜120 kg·cm/cm |
| Flexural modulus | | ASTM D-790 | 无水｜122000 kg/cm2 |
| Flexural modulus | | ASTM D-790 | 1.9%水｜72000 kg/cm2 |
| Flexural modulus | | ASTM D-790 | 无水｜63000 kg/cm2 |
| Flexural modulus | | ASTM D-790 | 1.9%水｜45000 kg/cm2 |
| Flexural modulus | | ASTM D-790 | 无水｜140000 kg/cm2 |
| Flexural modulus | | ASTM D-790 | 1.9%水｜120000 kg/cm2 |
| Rockwell hardness | | ASTM D-785 | 无水｜95 M-标度 |
| Rockwell hardness | | ASTM D-785 | 1.9%水｜- M-标度 |
| Rockwell hardness | | ASTM D-785 | 无水｜121 R-标度 |
| elongation at break | | ASTM D-638 | 无水｜5 % |
| elongation at break | | ASTM D-638 | 1.9%水｜5 % |
| Impact strength of cantilever beam gap | | ASTM D-256 | 无水｜12.5 kg·cm/cm |
| Impact strength of cantilever beam gap | | ASTM D-256 | 1.9%水｜15 kg·cm/cm |
| Impact strength of cantilever beam gap | | ASTM D-256 | 无水｜12.5 kg·cm/cm2 |
| Impact strength of cantilever beam gap | | ASTM D-256 | 1.9%水｜15 kg·cm/cm2 |
| Impact strength of cantilever beam gap | | ASTM D-256 | 无水｜15 kg·cm/cm |
| Impact strength of cantilever beam gap | | ASTM D-256 | 1.9%水｜20 kg·cm/cm |
| Impact strength of cantilever beam gap | | ASTM D-256 | 无水｜98 kg·cm/cm |
| shearing strength | | ASTM D-732 | 无水｜940 kg/cm2 |
| shearing strength | | ASTM D-732 | 1.9%水｜750 kg/cm2 |
| Rockwell hardness | | ASTM D-785 | 1.9%水｜- R-标度 |
| bending strength | | ASTM D-790 | 无水｜2900 kg/cm2 |
| bending strength | | ASTM D-790 | 1.9%水｜1850 kg/cm2 |
| bending strength | | ASTM D-790 | 无水｜16000 kg/cm2 |
| bending strength | | ASTM D-790 | 1.9%水｜- kg/cm2 |
| bending strength | | ASTM D-790 | 无水｜3300 kg/cm2 |
| bending strength | | ASTM D-790 | 1.9%水｜- kg/cm2 |
| tensile strength | | ASTM D-638 | 无水｜2000 kg/cm2 |
| tensile strength | | ASTM D-638 | 1.9%水｜1300 kg/cm2 |
| tensile strength | | ASTM D-638 | 无水｜1200 kg/cm2 |
| tensile strength | | ASTM D-638 | 1.9%水｜- kg/cm2 |
| tensile strength | | ASTM D-638 | 无水｜2900 kg/cm2 |
| tensile strength | | ASTM D-638 | 1.9%水｜- kg/cm2 |
| compressive strength | | ASTM D-695 | 无水｜1900 kg/cm2 |
| compressive strength | | ASTM D-695 | 1.9%水｜- kg/cm2 |
| compressive strength | | ASTM D-695 | 无水｜1000 kg/cm2 |
| compressive strength | | ASTM D-695 | 1.9%水｜- kg/cm2 |
| compressive strength | | ASTM D-695 | 无水｜2600 kg/cm2 |
| compressive strength | | ASTM D-695 | 1.9%水｜- kg/cm2 |
| Other performance | Test Condition | Test Method | Test Result |
|---|
| filler content | | | 无水｜45 wt% |
| filler content | | | 1.9%水｜- wt% |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Dissipation Factor | | ASTM D-150 | 无水｜0.02 |
| Dissipation Factor | | ASTM D-150 | 1.9%水｜0.06 |
| dielectric strength | | ASTM D-149 | 无水｜19 KV/mm |
| dielectric strength | | ASTM D-149 | 1.9%水｜15 KV/mm |
| dielectric constant | | ASTM D-150 | 无水｜4.2 |
| dielectric constant | | ASTM D-150 | 1.9%水｜4.5 |
| dielectric constant | | ASTM D-150 | 无水｜4.9 |
| dielectric constant | | ASTM D-150 | 1.9%水｜7.4 |
| Volume resistivity | | ASTM D-257 | 无水｜1015 Ω.cm |
| Volume resistivity | | ASTM D-257 | 1.9%水｜1012 Ω.cm |
| Dissipation Factor | | ASTM D-150 | 无水｜0.03 |
| Dissipation Factor | | ASTM D-150 | 1.9%水｜0.16 |
| arc resistance | | ASTM D-495 | 无水｜104 S |
| arc resistance | | ASTM D-495 | 1.9%水｜119 S |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| UL-94 flame retardant grade | | UL 94 | 无水｜HB |
| UL-94 flame retardant grade | | UL 94 | 1.9%水｜- |
| Heat distortion temperature | | ASTM D-648 | 无水｜225 °C |
| Heat distortion temperature | | ASTM D-648 | 1.9%水｜- °C |
| melting temperature | | 差示扫描测热计DSC | 无水｜225 °C |
| specific heat | | | 无水｜0.31 Cal/g·℃ |
| specific heat | | | 1.9%水｜- Cal/g·℃ |
| Linear coefficient of thermal expansion | | ASTM D-696 | 无水｜2-3 ×10-5cm/cm/℃ |
| Linear coefficient of thermal expansion | | ASTM D-696 | 1.9%水｜- ×10-5cm/cm/℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.