PPA AF4133-NC SOLVAY USA

Form：Granules | Grade：Injection grade

Properties:

High temperature resistanenhanceThermal stabilityFiller: Glass fiber reinfFiller by weight

Typical Applications:

Automotive componentsSports equipmentVehicle electronicscurrencyLawn and garden equipmentLaptop caseIndustrial componentsValves/valve componentsMetal substitutionIndustrial applicationsThick wall accessories (components)PhoneApplication in the automotive fieldMachine/mechanical componentsElectrical/Electronic ApplicationsParts under the hood of a car

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive components \| Sports equipment \| Vehicle electronics \| currency \| Lawn and garden equipment \| Laptop case \| Industrial components \| Valves/valve components \| Metal substitution \| Industrial applications \| Thick wall accessories (components) \| Phone \| Application in the automotive field \| Machine/mechanical components \| Electrical/Electronic Applications \| Parts under the hood of a car
Properties:	High temperature resistan \| enhance \| Thermal stability \| Filler: Glass fiber reinf \| Filler by weight

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
transmissivity	1070nm:1.60mm	ASTM D1003	>20	%
transmissivity	transmissivity	940nm:1.60mm	ASTM D1003	>20	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	59	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	67	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	3.2mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ASTM D638	11700	Mpa
Tensile strain	Break,23°C	ISO 527-2	2.6	%
	Tensile strain	Break,24°C	ISO 527-2	4.3	%
		Tensile strain	Break,150°C	ISO 527-2	6.6	%
		Tensile strain	Tensile strain	Break,175°C	ISO 527-2	6.6	%
Bending modulus		ASTM D790	11000	Mpa
Tensile modulus	23°C	ISO 527-2	12600	Mpa
	Tensile modulus	100°C	ISO 527-2	6830	Mpa
		Tensile modulus	150°C	ISO 527-2	5310	Mpa
		Tensile modulus	Tensile modulus	175°C	ISO 527-2	4830	Mpa
tensile strength		ASTM D638	200	Mpa
	tensile strength	Break,23°C	ISO 527-2	211	Mpa
		tensile strength	Break,24°C	ISO 527-2	125	Mpa
			tensile strength	Break,150°C	ISO 527-2	87.6	Mpa
			tensile strength	tensile strength	Break,175°C	ISO 527-2	79.3	Mpa
elongation	Break	ASTM D638	2.5	%
Bending modulus	23°C	ISO 178	10400	Mpa
	Bending modulus	100°C	ISO 178	7170	Mpa
		Bending modulus	150°C	ISO 178	4620	Mpa
		Bending modulus	Bending modulus	175°C	ISO 178	4210	Mpa
bending strength		ASTM D790	290	Mpa
	bending strength	23°C	ISO 178	296	Mpa
		bending strength	100°C	ISO 178	177	Mpa
			bending strength	150°C	ISO 178	111	Mpa
			bending strength	bending strength	175°C	ISO 178	99.3	Mpa
compressive strength		ASTM D695	179	Mpa
shear strength		ASTM D732	89.6	Mpa
Poisson's ratio			7.58	0.41
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Annealed,3.20mm	ASTM D648	320	°C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	294	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed,3.20mm	ASTM D648	300	°C
Continuous use temperature		ASTM D3045	210	°C
Melting temperature		ISO 11357-3	327	°C
Melting temperature	Melting temperature		ASTM D570	327	°C
Linear coefficient of thermal expansion	MD：0to100°C	ASTME831	2E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD：100to200°C	ASTME831	1.5E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD：0to100°C	ASTME831	7.6E-05	cm/cm/°C
			Linear coefficient of thermal expansion	TD：100to200°C	ASTME831	1.2E-04	cm/cm/°C
			Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：100to200°C	ASTME831	1.2E-04	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	MD	ASTM D955	0.50	%
Shrinkage rate	Shrinkage rate	TD	ASTM D955	1.0	%
Water absorption rate	24hr	ASTM D570	0.29	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		ASTM D257	2E+16	ohms·cm
Dielectric strength	1.60mm	ASTM D149	20	KV/mm
Dielectric constant	60Hz	ASTM D150	3.80
Dielectric constant	Dielectric constant	1MHz	ASTM D150	3.60
Dissipation factor	60Hz	ASTM D150	4E-03
Dissipation factor	Dissipation factor	1MHz	ASTM D150	0.012

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.