Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 12 g/10min |
| Shrinkage rate | | ASTM D955 | 0.50-0.80 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 117 |
| other | Test Condition | Test Method | Test Result |
|---|
| characteristic | | | 耐化学性良好 耐低温撞击 超高韧性 |
| purpose | | | 电气 电子应用领域 手机 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 117 |
| Flexural modulus | | ASTM D790/ISO 178 | 2060 kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 88.3 kg/cm²(MPa)[Lb/in²] |
| tensile strength | | ASTM D638 | 56.9 Mpa |
| elongation | | ASTM D638 | 130 % |
| Flexural modulus | | ASTM D790 | 2160 Mpa |
| bending strength | | ASTM D790 | 88.3 Mpa |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 1.20 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 130 °C |
| RTI Elec | | UL 746 | 80.0 °C |
| RTI Imp | | UL 746 | 80.0 °C |
| RTI Str | | UL 746 | 80.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.