PC DMX9455A-BK1B413T SABIC INNOVATIVE US

Form：Granules

Properties:

Scratch resistantcopolymerizationwear resistantFlame retardanttransparent

Typical Applications:

Bottle capFitness equipmentAutomotive sectorElectronic fieldElectrical field

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Bottle cap \| Fitness equipment \| Automotive sector \| Electronic field \| Electrical field
Properties:	Scratch resistant \| copolymerization \| wear resistant \| Flame retardant \| transparent

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	V-notch Edgew 80103 sp=62mm，-30℃	ISO 179/1eA	3	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	V-notch Edgew 80103 sp=62mm，23℃	ISO 179/1eA	3	kJ/m²
Impact strength of cantilever beam gap	30℃	ASTM D256	30	J/m
	Impact strength of cantilever beam gap	80103，30℃	ISO 180/1A	4	kJ/m²
		Impact strength of cantilever beam gap	23℃	ASTM D256	30	J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	80103，23℃	ISO 180/1A	5	kJ/m²
Suspended wall beam without notch impact strength	23℃	ASTM D4812	NB	J/m
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	80103，23℃	ISO 180/1U	NB	kJ/m²
Total energy at 23 ℃ (73 ℉)		ASTM D3763	30
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	50 mm/min	ASTM D638	2900	Mpa
Tensile modulus	Tensile modulus	1 mm/min	ISO 527	2450	Mpa
Bending modulus	2 mm/min	ISO 178	2450	Mpa
Fracture (brk)	50 mm/min	ISO 527	40	%
Fracture (brk)	Fracture (brk)	Type I, 50 mm/min	ASTM D638	70	%
Yield (yld)	50 mm/min，Yield	ISO 527	7	%
Yield (yld)	Yield (yld)	Type I, 50 mm/min，Yield	ASTM D638	7	%
Fracture (brk)	Type I, 50 mm/min	ASTM D638	65	Mpa
Fracture (brk)	Fracture (brk)	50 mm/min	ISO 527	60	Mpa
Yield (yld)	50 mm/min，Yield	ISO 527	80	Mpa
Yield (yld)	Yield (yld)	Type I, 50 mm/min，Yield	ASTM D638	80	Mpa
Bending modulus	1.3 mm/min, 50 mm span	ASTM D790	2600	Mpa
Yield (yld)	2 mm/min，Yield	ISO 178	108	Mpa
Yield (yld)	Yield (yld)	1.3 mm/min, 50 mm span，Yield	ASTM D790	120	Mpa
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Wear resistance		ASTM D 1044	10
Wear resistance	Wear resistance		Internal	10
Bi Rong		ASTM D792	0.85
Water absorption rate	50% RH, 24 hrs	ASTM D 570	0.04	%
	Water absorption rate	23°C / 50% RH	ISO 62	0.13	%
		Water absorption rate	23°C/sat	ISO 62	0.27	%
			Water absorption rate	equilibrium, 23C	ASTM D570	0.28	%
				Water absorption rate	50% RH, equilib	ASTM D570	0.13	%
				Water absorption rate	Water absorption rate	24 hours	ASTM D570	0.08	%
Vertical (Flow)	3.2 mm	Internal	0.5-0.8	%
melt mass-flow rate	300℃/1.2 kg	ASTM D1238	14.5
Melt Volume Flow Rate (MVR)		ISO 1133	13

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PC DMX9455A-BK1B413T SABIC INNOVATIVE US

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index