'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PPO N190X-111 SABIC INNOVATIVE SHANGHAI
160
Form：Granules
Properties:
High temperature resistanGlass fiber reinforced
Typical Applications:
Electrical components
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | Electrical components |
| Properties: | High temperature resistan | Glass fiber reinforced |
Certificates
No Data...
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 720 | J/m |
| Dart impact | 23°C, Total Energy | ASTM D3763 | 50.0 | J |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| Extreme Oxygen Index | ASTM D2863 | 39 | % | |
| UL flame retardant rating | 3.0 mm | UL 94 | 5VA | |
| 1.5 mm | UL 94 | V-0 | ||
| 1.0 mm | UL 94 | HB | ||
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Tensile modulus | --2 | ASTM D638 | 2580 | Mpa |
| -- | ISO 527-2/1 | 2600 | Mpa | |
| tensile strength | Yield3 | ASTM D638 | 60.0 | Mpa |
| Yield | ISO 527-2/50 | 58.0 | Mpa | |
| Break3 | ASTM D638 | 47.0 | Mpa | |
| Break | ISO 527-2/50 | 50.0 | Mpa | |
| elongation | Yield3 | ASTM D638 | 3.6 | % |
| Yield | ISO 527-2/50 | 3.2 | % | |
| Break3 | ASTM D638 | 9.0 | % | |
| Break | ISO 527-2/50 | 9.2 | % | |
| Bending modulus | 50.0 mm Span4 | ASTM D790 | 2500 | Mpa |
| 100 mm Span5 | ASTM D790 | 2300 | Mpa | |
| --6 | ISO 178 | 2350 | Mpa | |
| bending strength | --6,7 | ISO 178 | 87.0 | Mpa |
| Yield, 50.0 mm Span4 | ASTM D790 | 98.0 | Mpa | |
| Yield, 100 mm Span5 | ASTM D790 | 91.0 | Mpa | |
| Taber abraser | 1000 Cycles, 1000 g, CS-17 Wheel | ASTM D1044 | 76.0 | mg |
| injection | Test Condition | Test Method | Test Result | Test Unit |
| Temperature at the front of the material cylinder | 240 to 275 | °C | ||
| Spray nozzle temperature | 250 to 275 | °C | ||
| Temperature in the middle of the barrel | 225 to 270 | °C | ||
| Temperature at the rear of the barrel | 215 to 265 | °C | ||
| Suggested injection volume | 30 to 70 | % | ||
| Suggested maximum moisture content | 0.020 | % | ||
| drying time | 3.0 to 4.0 | hr | ||
| drying temperature | 75 to 80 | °C | ||
| Processing (melt) temperature | 250 to 275 | °C | ||
| Mold temperature | 55 to 75 | °C | ||
| Back pressure | 0.300 to 0.700 | Mpa | ||
| Screw speed | 20 to 100 | rpm | ||
| Exhaust hole depth | 0.038 to 0.051 | mm | ||
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Hot deformation temperature | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 95.0 | °C |
| 0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span8 | ISO 75-2/Bf | 95.0 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 78.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 86.0 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8 | ISO 75-2/Af | 82.0 | °C | |
| Vicat softening temperature | -- | ASTM D15259 | 104 | °C |
| -- | ISO 306/B120 | 107 | °C | |
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | ASTM E831 | 7.7E-5 | cm/cm/°C |
| Across Flow : -40 to 40°C | ASTM E831 | 8.1E-5 | cm/cm/°C | |
| thermal conductivity | ASTM C177 | 0.24 | W/m/K | |
| RTI | UL 746 | 95.0 | °C | |
| RTI Imp | UL 746 | 80.0 | °C | |
| RTI Elec | UL 746 | 95.0 | °C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| melt mass-flow rate | 280°C/5.0 kg | ASTM D1238 | 20 | g/10 min |
| Melt Volume Flow Rate (MVR) | 280°C/5.0 kg | ISO 1133 | 23.0 | cm3/10min |
| Shrinkage rate | 3.20 mm，Flow | Internal Method | 0.50 - 0.70 | % |
| Water absorption rate | 24 hr | ASTM D570 | 0.080 | % |
| Outdoor applicability | UL 746C | f1 | ||
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Hot wire ignition | UL 746 | PLC 2 | ||
| High voltage arc tracing rate | UL 746 | PLC 4 | ||
| High arc combustion index | UL 746 | PLC 2 | ||
| Compared to the anti leakage trace index | UL 746 | PLC 1 | ||
| Arc resistance | ASTM D495 | PLC 7 | ||
| Dissipation factor | 100 kHz | ASTM D150 | 5.5E-3 | |
| 100 Hz | ASTM D150 | 0.013 | ||
| Dielectric constant | 100 kHz | ASTM D150 | 2.60 | |
| 100 Hz | ASTM D150 | 2.74 | ||
| Dielectric strength | 3.20 mm, in Oil | ASTM D149 | 19 | KV/mm |
| Volume resistivity | ASTM D257 | 1.8E+16 | ohms·cm | |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | R-Scale | ASTM D785 | 120 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.