Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| | | 按重量计算的混合比:100,按容量计算的混合比:100 |
| | | 按重量计算的混合比:40,按容量计算的混合比:40 |
| Thermosetting mixed viscosity | | ASTMD4878 | 3900 cP |
| stripping time | | 内部方法 | 480到720 min |
| GelTime | | ASTMD2971 | 40.0 min |
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD4669 | 1.07 g/cm³ |
| Shrinkage rate | | ASTMD2566 | 0.20到0.30 % |
| Weight Percubicinch | | | 18 g |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore A | ASTMD2240 | 70 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTMD638 | 4.14 MPa |
| tensile strength | | ASTMD638 | 13.1 MPa |
| elongation | Break | ASTMD638 | 580 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 无断裂 |
| Suspended wall beam without notch impact strength | | ASTMD256 | 无断裂 |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tear strength | | ASTMD624 | 24.9 kN/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.