Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D-1238 | 2.0 g/10min |
| film thickness | | | 25 μm |
| other | Test Condition | Test Method | Test Result |
|---|
| | | 加工性, 滑爽性，光泽性 |
| purpose | | | 普通薄膜 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D-1505 | 0.919 g/cm³ |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strength (yield point) | | ASTM D-882 | 120 kg/cm2 |
| Tensile strength (yield point) | | ASTM D-882 | 110 kg/cm2 |
| elongation at break | | ASTM D-882 | 650 % |
| elongation at break | | ASTM D-882 | 800 % |
| Tensile strength (fracture point) | | ASTM D-882 | 380 kg/cm2 |
| Tensile strength (fracture point) | | ASTM D-882 | 340 kg/cm2 |
| Tensile modulus | | ASTM D-882 | 2000 kg/cm2 |
| Tensile modulus | | ASTM D-882 | 2500 kg/cm2 |
| tear strength | | ASTM D-1004 | 125 kg/cm |
| tear strength | | ASTM D-1004 | 105 kg/cm |
| Sharp Point Impact Strength | | ASTM D-1709 | 3.7 g/μm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 0.919 |
| melt mass-flow rate | | ASTM D1238/ISO 1133 | 1.8 g/10min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ASTM D1525/ISO R306 | 102 ℃（℉） |
| Low temperature brittleness temperature | | ASTM D-746 | <-70 °C |
| softening point | | ASTM D-1525 | 102 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.