PP Moharamplast PP MP-COAT 9010
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTMD792 | 0.910 g/cm³ | |
| melt mass-flow rate | ASTMD1238 | 0.80 g/10min | |
| Resistance to environmental stress cracking | ASTMD1693A | >5000 hr | |
| ASTMD1693B | >5000 hr | ||
| ASTMD1693C | >5000 hr | ||
| ASTMD1693C | >5000 hr | ||
| density | ASTMD792 | 0.910 g/cm³ | |
| melt mass-flow rate | ASTMD1238 | 0.80 g/10min | |
| Resistance to environmental stress cracking | ASTMD1693A | >5000 hr | |
| ASTMD1693B | >5000 hr |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ASTMD2240 | >60 | ||
| ASTMD2240 | >60 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | Yield | ASTMD638 | >21.6 MPa |
| Yield | ASTMD638 | >21.6 MPa | |
| Break | ASTMD638 | >29.4 MPa | |
| elongation | Break | ASTMD638 | >1200 % |
| tensile strength | Break | ASTMD638 | >29.4 MPa |
| elongation | Break | ASTMD638 | >1200 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ImpactResistance | ISO21809-1 | >100 J/cm | |
| ISO21809-1 | >100 J/cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| brittle temperature | ASTMD746 | <-40.0 °C | |
| melting temperature | ASTMD2117 | >160 °C | |
| brittle temperature | ASTMD746 | <-40.0 °C | |
| vicat | ASTMD1525 | 140 °C | |
| ASTMD1525 | 140 °C | ||
| melting temperature | ASTMD2117 | >160 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.