'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PPS 6165A6 SD3002 CELANESE USA
161
Form：Granules | Grade：Injection grade
Properties:
Glass fiber reinforcedFlame retardantstandardHigh temperature resistanFiller: Glass mineralFiller by weightFiller by weight
Typical Applications:
Fiber gradePump partsShellElectrical/Electronic Applications
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | Fiber grade | Pump parts | Shell | Electrical/Electronic Applications |
| Properties: | Glass fiber reinforced | Flame retardant | standard | High temperature resistan | Filler: Glass mineral | Filler by weight | Filler by weight |
Certificates
No Data...
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 20 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 6.0 | kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 7.0 | kJ/m² |
| 23°C | ISO 179/1eA | 7.0 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 20 | kJ/m² |
| 23°C | ISO 179/1eU | 20 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 6.0 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 0.75mm | UL 94 | V-0 | |
| 1.5mm | UL 94 | V-0 | ||
| Basic Performance | Test Condition | Test Method | Test Result | Test Unit |
| Water absorption rate | 23℃ | ISO 62 | 0.02 | % |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| tensile strength | Break,23°C | ASTM D638 | 114 | Mpa |
| Impact strength of cantilever beam gap | 23℃ | ISO 180/1A | 6 | kJ/m² |
| tensile strength | ISO 527-1 | 130 | Mpa | |
| elongation | Break | ISO 527-1 | 1.2 | % |
| Bending modulus | ISO 178 | 18800 | Mpa | |
| bending strength | ISO 178 | 210 | Mpa | |
| Rockwell hardness | ISO 2039-2 | 100 | M-scale | |
| Tensile modulus | ISO 527-1 | 19000 | Mpa | |
| tensile strength | Break | ISO 527-2/1A/5 | 130 | Mpa |
| elongation | Break,23°C | ASTM D638 | 1.3 | % |
| Tensile strain | Break | ISO 527-2/1A/5 | 1.2 | % |
| Bending modulus | 23°C | ISO 178 | 18800 | Mpa |
| bending strength | ISO 178 | 210 | Mpa | |
| Tensile modulus | ISO 527-2/1A/1 | 19000 | Mpa | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Hot deformation temperature | 1.8MPa,Unannealed | ASTM D648 | 266 | °C |
| 0.45MPa,Annealed | ASTM D648 | 280 | °C | |
| UL flame retardant rating | 0.750mm | UL 94 | V-0 | |
| Hot deformation temperature | 1.80Mpa | ISO 75-1 | 270 | °C |
| 1.8MPa,Unannealed | ISO 75-2/A | 270 | °C | |
| 8.0MPa,Unannealed | ISO 75-2/C | 215 | °C | |
| Glass transition temperature | ISO 11357-2 | 90.0 | °C | |
| Melting temperature | ISO 11357-3 | 280 | °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.9E-05 | cm/cm/°C |
| TD | ISO 11359-2 | 2.4E-05 | cm/cm/°C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Specific volume | ASTM D792 | 0.502 | cm³/g | |
| density | ASTM D792 | 2.00 | g/cm³ | |
| ISO 1183 | 1.95 | g/cm³ | ||
| Shrinkage rate | ISO 2577 | 0.2-0.6 | % | |
| density | ISO 1183 | 1.95 | g/cm³ | |
| Shrinkage rate | MD | ASTM D955 | 0.10-0.20 | % |
| TD | ASTM D955 | 0.30-0.50 | % | |
| TD | ISO 294-4 | 0.30-0.70 | % | |
| SpecificHeatCapacity of Melt | Internal Method | 1600 | J/kg/°C | |
| Water absorption rate | Saturation,23°C | ISO 62 | 0.020 | % |
| Shrinkage rate | MD | ISO 294-4 | 0.20-0.60 | % |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Dissipation factor | 1MHz | IEC 60250 | 2E-03 | |
| Surface resistivity | IEC 60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC 60093 | >1.0E+15 | ohms·cm | |
| Dielectric strength | IEC 60243-1 | 25 | KV/mm | |
| Dielectric constant | 1kHz | ASTM D150 | 4.50 | |
| 1MHz | ASTM D150 | 4.50 | ||
| Relative permittivity | 1MHz | IEC 60250 | 5.60 | |
| Dissipation factor | 1kHz | ASTM D150 | 1E-03 | |
| 1MHz | ASTM D150 | 9E-04 | ||
| Arc resistance | ASTM D495 | 182 | sec | |
| Compared to the anti leakage trace index | IEC 60112 | PLC 3 | ||
| Volume resistivity | ASTM D257 | 1E+16 | ohms·cm | |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | M-Scale | ISO 2039-2 | 100 | |
| M-Scale | ASTM D785 | 100 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.