PEEK Larpeek 10 G/30

Properties:
Filler
glass fiber reinforced material
30%
filler by weight
Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
Water absorption rate		ISO 62	0.060 %
density		ISO 1183	1.50 g/cm³
Shrinkage rate		ISO 294-4	0.55to0.85 %
Shrinkage rate	Shrinkage rate		ISO 294-4	0.20to0.45 %

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	V-0
UL flame retardant rating	UL flame retardant rating		UL 94	V-0
Burning wire flammability index		IEC 60695-2-12	960 °C
Hot filament ignition temperature		IEC 60695-2-13	875 °C
UL flame retardant rating		UL 94	V-1

Mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1	11500 MPa
	Tensile modulus		ISO 527-2/1	11500 MPa
		Tensile modulus		ISO 527-2/1	11000 MPa
		Tensile modulus	Tensile modulus		ISO 527-2/1	10500 MPa
Tensile strain		ISO 527-2/5	2.3 %
Tensile strain	Tensile strain		ISO 527-2/5	2.5 %
Tensile modulus		ISO 527-2/1	10500 MPa
tensile strength		ISO 527-2/5	175 MPa
	tensile strength		ISO 527-2/5	165 MPa
		tensile strength		ISO 527-2/5	155 MPa
			tensile strength		ISO 527-2/5	135 MPa
			tensile strength	tensile strength		ISO 527-2/5	110 MPa
Tensile strain		ISO 527-2/5	2.2 %
	Tensile strain		ISO 527-2/5	2.2 %
	Tensile strain	Tensile strain		ISO 527-2/5	2.3 %

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO 179/1eA	10 kJ/m²
Impact strength of simply supported beam without notch		ISO 179/1eU	65 kJ/m²

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ISO 75-2/B	295 °C
Heat distortion temperature	Heat distortion temperature		ISO 75-2/A	290 °C
Continuous use temperature			230 °C
vicat		ISO 306/B50	>300 °C
Linear coefficient of thermal expansion		ISO 11359-2	1.5E-05 cm/cm/°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.