Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.30 g/cm³ |
| Apparent density | | ASTMD1895B | 0.15 g/cm³ |
| MoistureContent-GSRF | | | 2.0to3.0 % |
| ParticleSizeDistribution-D | | | <130.0 µm |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTMD785 | 125 |
| | ASTMD2240 | 95 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| WeightLossonHeating | | 内部方法 | 570 °C |
| WeightLossonHeating | | 内部方法 | 520 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTMD638 | 5900 MPa |
| tensile strength | | ASTMD638 | 160 MPa |
| Compression Modulus | | ASTMD695 | 5900 MPa |
| compressive strength | | ASTMD695 | 390 MPa |
| elongation | | ASTMD638 | 3.0 % |
| Flexural modulus | | ASTMD790 | 6500 MPa |
| bending strength | | ASTMD790 | 220 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 21 J/m |
| Impact strength of cantilever beam gap | | ASTMD256 | 600 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTMD257 | 1E+15 ohms |
| Volume resistivity | | ASTMD257 | 1E+15 ohms·cm |
| arc resistance | | ASTMD495 | 185 sec |
| dielectric strength | | ASTMD149 | 23 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 440 °C |
| Continuous use temperature | | UL746B | 400 °C |
| Glass Transition Temperature | | 内部方法 | 467 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.