| physical property | Test Condition | Test Method | Test Result |
|---|
| Melt volume flow rate | | ISO 1133 | 20.0 cm3/10min |
| Shrinkage rate | | ISO 294-4 | 0.60-0.80 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO 2039-2 | 103 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | | 20 CM |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | | 15 KJ/m |
| Flexural modulus | | | 2450 Mpa |
| Tensile modulus | | ISO 527-2 | 2300 Mpa |
| tensile strength | | ISO 527-2 | 45.0 Mpa |
| Flexural modulus | | ISO 178 | 2450 Mpa |
| bending strength | | ISO 178 | 73.0 Mpa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | | 81 °C |
| UL flame retardant rating | | UL 94 | HB |
| Heat distortion temperature | | ISO 75-2/Af | 81.0 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 7E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.