| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 0.940 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 2.6 g/10min |
| Ionic type | | | Lithium |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTMD2240 | 68 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Haze ratio | | ASTM D1003 | 4.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 15.2 MPa |
| tensile strength | | ASTMD638 | 26.2 MPa |
| elongation | | ASTMD638 | 290 % |
| Flexural modulus | | ASTM D790 | 420 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D1822 | 525 kJ/m² |
| Impact strength of cantilever beam gap | | ASTM D1822 | 462 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ASTMD1525 | 63.0 °C |
| melting temperature | | ASTMD3418 | 91.0 °C |
| FreezingPoint | | ASTM D3418 | 48 °C |
| FreezingPoint | | ISO 3146 | 48 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.