ABS HH-106 INEOS STYRO THAILAND

Form：Granules | Grade：Heat resistant grade

Properties:

heat-resisting

Typical Applications:

Automotive interior partsElectronic fieldApplication in the automotive field

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive interior parts \| Electronic field \| Application in the automotive field
Properties:	heat-resisting

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179	190	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179	100	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Nominal tensile fracture strain	23°C	ISO 527-2	9.0	%
elongation	Break	ASTM D638	3.0	%
Tensile strain	Yield,23°C	ISO 527-2	3.0	%
tensile strength	Yield,23°C	ISO 527-2	51.0	Mpa
tensile strength	tensile strength	Yield,23°C	ASTM D638	52.0	Mpa
Tensile modulus		ISO 527-2	2400	Mpa
Tensile modulus	Tensile modulus		ASTM D638	2500	Mpa
Ball Pressure Test		ISO 2039-1	102	Mpa
Bending modulus		ASTM D790	2400	Mpa
Bending modulus	Bending modulus		ISO 178	2400	Mpa
bending strength		ASTM D790	77.2	Mpa
bending strength	bending strength		ISO 178	72.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	--	ISO 306/B50	106	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/A50	115	°C
Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	99.0	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Annealed	ISO 75-2/B	107	°C
Maximum operating temperature			85	°C
thermal conductivity		DIN 52612	0.17	W/m/K
Linear coefficient of thermal expansion	MD	ISO 11359-2	9E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.25	%
Shrinkage rate		ISO 294-4	0.40-0.70	%
Shrinkage rate	Shrinkage rate	MD	ASTM D955	0.55	%
Melt Volume Flow Rate (MVR)	220°C/10.0kg	ISO 1133	7.00	cm3/10min
melt mass-flow rate	220°C/10.0kg	ASTM D1238	7.0	g/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric strength	1.50mm	IEC 60243-1	39	KV/mm
Volume resistivity		IEC 60093	1E+15	ohms·cm
Volume resistivity	Volume resistivity		ASTM D257	>1.0E+15	ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.