PA6

PA6 Zytel® 73G40T NC010 DUPONT SHENZHEN

Properties:
Low temperature resistancFiller: Glass fiber reinf40% filler by weight
Usages:
Mirror frameElectronic and electrical components
Compare View Prices

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	110 kJ/m²

flammability	Test Condition	Test Method	Test Result
FMVSS flammability		FMVSS302	B
Burning rate	1.00mm	ISO 3795	<100 mm/min

mechanical properties	Test Condition	Test Method	Test Result
Tensile strain	Break	ISO 527-2	3.8 %
tensile strength	Break	ISO 527-2	210 Mpa
Tensile modulus		ISO 527-2	12500 Mpa

thermal performance	Test Condition	Test Method	Test Result
Melting temperature		ISO 11357-3	220 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	215 °C

Physical properties	Test Condition	Test Method	Test Result
MeltViscosity	280°C,1000sec^-1	ISO 11443	190000 mPa·s
Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	1.5 %
Water absorption rate	Water absorption rate	Saturation,23°C,2.00mm	ISO 62	5.3 %
Shrinkage rate	MD	ISO 294-4	0.10 %
Shrinkage rate	Shrinkage rate	TD	ISO 294-4	0.50 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

PA6 Zytel® 73G40T NC010 DUPONT SHENZHEN

Technical Data Sheet