Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.15 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 5.0 g/10min |
| Shrinkage rate | | ASTM D955 | 0.50to0.80 % |
| melt mass-flow rate | | ASTM D1238 | 5.0 g/10min |
| density | | ASTM D792 | 1.15 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.50to0.80 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ASTM D790 | 64.0 MPa |
| elongation | Break | ASTM D638 | 140 % |
| Flexural modulus | | ASTM D790 | 1850 MPa |
| tensile strength | | ASTM D638 | 46.0 MPa |
| Flexural modulus | | ASTM D790 | 1850 MPa |
| bending strength | | ASTM D790 | 64.0 MPa |
| tensile strength | | ASTM D638 | 46.0 MPa |
| elongation | Break | ASTM D638 | 140 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 650 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 650 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC 60093 | >1.0E+15 ohms·cm |
| Surface Resistivity | | IEC 60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC 60093 | >1.0E+15 ohms·cm |
| Surface Resistivity | | IEC 60093 | >1.0E+15 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 90.0 °C |
| Heat distortion temperature | | ASTM D648 | 90.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.