Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 294-4 | 0.90 % |
| Shrinkage rate | | ISO 294-4 | 0.30 % |
| Water absorption rate | | ISO 62 | 0.90 % |
| Water absorption rate | | ISO 62 | 4.7 % |
| Water absorption rate | | ISO 62 | 1.5 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | ISO 3795 | 27 mm/min |
| Limiting Oxygen Index | | ISO 4589-2 | 24 % |
| FMVSS combustion rate | | FMVSS 302 | B |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 14000 Mpa |
| tensile strength | | ISO 527-2 | 225 Mpa |
| Tensile strain | | ISO 527-2 | 2.5 % |
| Flexural modulus | | ISO 178 | 12500 Mpa |
| bending strength | | ISO 178 | 340 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 90 kJ/m² |
| Multi axis Instrumented Impact Energy | | ISO 6603-2 | 4.40 J |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| Ejection Temperature | | | 210 °C |
| Thermal Conductivity of Melt | | | 0.25 W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC 62631-3-1 | > 1.0E+13 ohms·m |
| dielectric strength | | IEC 60243-1 | 25 KV/mm |
| Dissipation Factor | | IEC 62631-2-1 | 0.013 |
| Dissipation Factor | | IEC 62631-2-1 | 0.015 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 80 °C |
| Drying time - hot air dryer | | | 2.0 to 4.0 hr |
| Suggested maximum moisture content | | | 0.20 % |
| Processing (melt) temperature | | | 285 to 300 °C |
| Melt Temperature, Optimum | | | 295 °C |
| Temperature | | | 70 to 120 °C |
| Mold Temperature, Optimum | | | 100 °C |
| pressure holding | | | 50.0 to 100 Mpa |
| pressure holding | | | yes |
| Hold Pressure Time | | | 3.00 s/mm |
| Maximum Screw Tangential Speed | | | 12 m/min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 258 °C |
| Heat distortion temperature | | ISO 75-2/A | 255 °C |
| Glass Transition Temperature | | ISO 11357-2 | 80.0 °C |
| melting temperature | | ISO 11357-3 | 262 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare
View Prices