PA6

PA6 NYCOA Polyamide 512 NYCOA USA

Compare

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
transmissivity			90 %

Other performance	Test Condition	Test Method	Test Result
process temperature			250 °C

mechanical properties	Test Condition	Test Method	Test Result
Elongation at Break	23°C	ASTM D638	>=40 %
tensile strength	Yield，23°C	ASTM D638	86.0 MPa
bending strength	Yield，23°C	ASTM D790	99.0 MPa
Impact strength of cantilever beam gap	23°C	ASTM D256	46.0 J/m
Bending modulus	23°C	ASTM D790	2656 MPa

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature	Melting Temperature	ATMD789	221 °C
Hot deformation temperature	1.80MPaUnannealed	ASTM D648	68 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	(23°C,24hr)	ASTM D570	1.7 %
Shrinkage rate	MD	ASTM D995	1.5 %
density		ASTM D792	1.13 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Dielectric strength	耐电弧性	ASTM D495	190 s
Dielectric strength	Dielectric strength		ASTM D149	10.2 KV/mm

hardness	Test Condition	Test Method	Test Result
Rockwell hardness		ASTM D785	120 R

flame retardant performance	Test Condition	Test Method	Test Result
UL flame retardant rating		UL -94	V-2 6.00mm
	UL flame retardant rating		UL -94	V-2 3.00mm
		UL flame retardant rating		UL -94	V-2 1.50mm
		UL flame retardant rating	UL flame retardant rating		UL -94	V-2 0.71mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.