Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.70到1.80 g/cm³ |
| Apparent density | | ISO60 | 0.80到1.00 g/cm³ |
| PostShrinkage | | ISO2577 | 0.20到0.40 % |
| Shrinkage rate | | ISO2577 | 0.70到1.0 % |
| Shrinkage rate | | ISO2577 | 0.50到0.80 % |
| Water absorption rate | | ISO62 | <1.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| CompressionMoldingPressure | | | >10.0 MPa |
| CompressionMoldingTemperature | | | 160到180 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Bending stress | Injection | ISO178 | 90.0到110 MPa |
| compression stress | | ISO604 | 150到200 MPa |
| Flexural modulus | Compression Molded | ISO178 | 8000到9000 MPa |
| Flexural modulus | Injection | ISO178 | 8000到9000 MPa |
| Bending stress | Compression Molded | ISO178 | 70.0到90.0 MPa |
| Tensile modulus | Compression Molded | ISO527-2 | 4000到6000 MPa |
| Tensile modulus | Injection | ISO527-2 | 5000到7000 MPa |
| Tensile stress | | ISO527-2 | 30.0到50.0 MPa |
| Tensile stress | Injection | ISO527-2 | 50.0到60.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | Compression Molded | ISO179/1eA | 1.5到2.5 kJ/m² |
| Charpy Notched Impact Strength | Injection | ISO179/1eA | 1.5到2.5 kJ/m² |
| Impact strength of simply supported beam without notch | Compression Molded | ISO179/1eU | 8.0到10 kJ/m² |
| Impact strength of simply supported beam without notch | Injection | ISO179/1eU | 10到12 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1.0E+11到1.0E+12 ohms |
| Volume resistivity | | IEC60093 | 1.0E+12到1.0E+13 ohms·cm |
| dielectric strength | | IEC60243-1 | 30到40 kV/mm |
| | IEC60250 | 5.007.00 |
| | IEC60250 | 4.005.00 |
| Dissipation Factor | | IEC60250 | 0.10到0.20 |
| Dissipation Factor | | IEC60250 | 0.030到0.050 |
| arc resistance | | ASTMD495 | PLC 4 |
| CTI | | IEC60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 180到200 °C |
| | ISO75-2/C | 80.0到110 °C |
| | ISO11359-2 | 2.0E-5到3.0E-5 cm/cm/°C |
| thermal conductivity | | ASTME1461 | 0.50到0.60 W/m/K |
| maximum service temperature | | IEC60216 | 190 °C |
| maximum service temperature | | IEC60216 | 150 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.