EA BCC Resins BC 100 Medium
0
CompareTechnical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Thermosetting mixed viscosity | ASTM D2393 | 80.0to120 cP | |
| Post curing time | 24 hr |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Gap filling ability | 200.0 µm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shear strength | ASTM D1002 | >10.0 MPa | |
| ASTM D732 | 18.0to28.0 MPa | ||
| ASTM D1002 | >20.0 MPa | ||
| ASTM D1002 | >22.0 MPa | ||
| ASTM D1002 | >25.0 MPa | ||
| ASTM D1002 | >18.0 MPa | ||
| ASTM D1002 | >12.0 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric strength | ASTM D149 | 25 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Glass Transition Temperature | ASTME228 | 122 °C | |
| melting temperature | 160to170 °C | ||
| Linear coefficient of thermal expansion | ASTM D696 | 9E-05 cm/cm/°C | |
| thermal conductivity | ASTMC177 | 0.10 W/m/K | |
| Usage temperature | -60-80 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.