AS(SAN) KIBISAN® PN-107L125 TAIWAN CHIMEI
698
- Properties:transparentHigh transparencyInjection moldingoneDry the material at 75-80twoThe temperature of the inthreeThe injection pressure iscm<sup>2<sup>fourMaintain a pressure of 40cm<sup>2<sup>fiveBack pressure is 5-15kgcm<sup>2<sup>sixThe mold temperature is bsevenDo not leave the hot melt
- Usages:chipcontainerHousehold goodsFood containers
- Certificates:ULMSDS
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | 23℃ | ISO 1183 | 1.06 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| hardness | H358/30 | ISO 2039-1 | 155 | n/mm² |
| tensile strength | 50 mm/min,yield | ISO 527 | 52 | Mpa |
| 50 mm/min,break | ISO 527 | 52 | Mpa | |
| Elongation rate | 50 mm/min | ISO 527 | 4 | % |
| bending strength | 2 mm/min | ISO 178 | 178 | Mpa |
| Bending modulus of elasticity | 2 mm/min | ISO 178 | 2.6 | GPa |
| IZOD impact strength | Notched | ISO 180/1A | 2 | kJ/m² |
| Charpy impact strength | Notched | ISO 179 | 2 | kJ/m² |
| Unnotched | ISO 179 | 18 | kJ/m² | |
| Scratch test | Notched | ISO 179/2C | 3 | kJ/m² |
| Unnotched | ISO 179/2D | 15 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vickers softening temperature | 1 Kg,50℃/hr | ISO 306 | 104 | ℃ |
| Hot deformation temperature | 1.8 MPa Unannealed | ISO 75 | 88 | ℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.