PA6 TG7S BASF GERMANY

Form：Granules | Grade：Injection grade

Properties:

Glass fiber reinforced

Typical Applications:

Engine parts

Supplier(0)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Engine parts
Properties:	Glass fiber reinforced

Certificates

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			可加工性良好良好的流动性良好的抗撞击性
purpose			汽车领域的应用座椅
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	-40℉，Break	ASTM D638	36400	psi
	tensile strength	176℉，Break	ASTM D638	14100	psi
	tensile strength	tensile strength	248℉，Break	ASTM D638	11200	psi
Tensile stress	-40℉，Break	ISO 527-1	36400	psi
	Tensile stress	176℉，Break	ISO 527-1	14100	psi
	Tensile stress	Tensile stress	248℉，Break	ISO 527-1	11200	psi
Fracture stress		ISO 527-1	25000	psi
Elongation at Break	-40℉	ASTM D638	3.9	%
	Elongation at Break	176℉	ASTM D638	6.7	%
	Elongation at Break	Elongation at Break	248℉	ASTM D638	7.0	%
Fracture strain		ISO 527-1	3.3	%
Bending modulus	73℉	ASTM D790	1.3E+06	psi
Bending modulus	Bending modulus	73℉	ISO 178	1.22E+06	psi
bending strength	73℉	ASTM D790	37700	psi
Charpy Notched Impact Strength	23℃	ISO 179/1eA	10.9	ft·lb/in
Impact strength of cantilever beam gap	-40℉	ISO 180	8.57	ft·lb/in
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	73℉	ISO 180	12.4	ft·lb/in
tensile strength	Break,150°C	ISO 527-2	66.0	Mpa
Tensile strain	Break,-40°C	ISO 527-2	3.9	%
	Tensile strain	Break,23°C	ISO 527-2	3.3	%
		Tensile strain	Break,80°C	ISO 527-2	6.7	%
			Tensile strain	Break,120°C	ISO 527-2	7.0	%
			Tensile strain	Tensile strain	Break,150°C	ISO 527-2	7.1	%
Bending modulus	23°C	ISO 178	8400	Mpa
tensile strength	Break,-40°C	ISO 527-2	251	Mpa
	tensile strength	Break,23°C	ISO 527-2	170	Mpa
		tensile strength	Break,80°C	ISO 527-2	97.0	Mpa
		tensile strength	tensile strength	Break,120°C	ISO 527-2	77.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Melting temperature			428	℉
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	203	°C
Melting temperature		ISO 3146	220	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.