PC/ABS T45 901510 COVESTRO SHANGHAI

Form：Granules | Grade：Injection grade

Properties:

Easy electroplating

Typical Applications:

Electrical fieldElectronic fieldFitness equipmentHousehold appliancesHousehold appliancesAutomotive sector

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electrical field \| Electronic field \| Fitness equipment \| Household appliances \| Household appliances \| Automotive sector
Properties:	Easy electroplating

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	-30°C	ISO 180/A	36	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/A	40	kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180	NoBreak
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180	NoBreak
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.9mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile strain	Break,23°C	ISO 527-2/50	>50	%
Tensile modulus	23°C	ISO 527-2/1	2100	Mpa
tensile strength	Yield,23°C	ISO 527-2/50	49.0	Mpa
tensile strength	tensile strength	Break,23°C	ISO 527-2/50	40.0	Mpa
Tensile strain	Yield,23°C	ISO 527-2/50	3.7	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	9E-05	cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	112	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	95.0	°C
Vicat softening temperature	--	ISO 306/B50	110	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	112	°C
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	8.5E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density	23°C	ISO 1183	1.10	g/cm³
Melt Volume Flow Rate (MVR)	260°C/5.0kg	ISO 1133	12.0	cm3/10min
Shrinkage rate	TD:260°C,3.00mm	ISO 2577	0.55-0.75	%
Shrinkage rate	Shrinkage rate	MD:260°C,3.00mm	ISO 2577	0.55-0.75	%
Water absorption rate	Saturation,23°C	ISO 62	0.70	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.20	%
MeltViscosity	260°C	ISO 11443-A	200	Pa·s
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	1E+16	ohms
Volume resistivity	23°C	IEC 60093	1E+16	ohms·cm
Dielectric strength	23°C,1.00mm	IEC 60243-1	35	KV/mm
Relative permittivity	23°C,100Hz	IEC 60250	3.10
Relative permittivity	Relative permittivity	23°C,1MHz	IEC 60250	3.00
Dissipation factor	23°C,100Hz	IEC 60250	3.5E-03
Dissipation factor	Dissipation factor	23°C,1MHz	IEC 60250	8.5E-03
Compared to the anti leakage trace index	SolutionA	IEC 60112		V

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.