PVC Alloy Geon™ HTX M6829 Geon Performance Solutions

Usages:
Electrical and electronic application fields communication equipment general
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C,3.18mm,Injection	ASTM D256A	370 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	3.0mm	UL 94	V-1

mechanical properties	Test Condition	Test Method	Test Result
elongation	Break	ASTM D638	20 %
Bending modulus		ASTM D790	2340 MPa
bending strength		ASTM D790	70.3 MPa
Tensile modulus		ASTM D638	2340 MPa
tensile strength	Yield	ASTM D638	39.3 MPa

thermal performance	Test Condition	Test Method	Test Result
RTI		UL 746	80.0 °C
RTI Imp		UL 746	70.0 °C
Hot deformation temperature	维卡软化点	ASTM D648	91 °C
	Hot deformation temperature	1.8MPa,Annealed,6.35mm	ASTM D648	86.1 °C
		Hot deformation temperature	1.8MPa,Unannealed,6.35mm	ASTM D648	77.2 °C
			Hot deformation temperature	0.45MPa,Annealed,6.35mm	ASTM D648	88.9 °C
			Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,6.35mm	ASTM D648	82.8 °C
RTI Elec		UL 746	80.0 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD	ASTM D955	0.40to0.50 %
Spiral flow length			86.4 cm
density		ASTM D792	1.16 g/cm³

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.