ABS 8434 SINOPEC SHANGHAI GAOQIAO
18
- Properties:heat-resistingHigh rigidity
- Usages:small home appliancesAutomotive sector
CompareTechnical Data Sheet
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 高光泽高耐热 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D-1238 | 3.9 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D638/ISO 527 | 41屈服 32断裂 kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 2 % | |
| bending strength | ASTM D790/ISO 178 | 75 kg/cm²(MPa)[Lb/in²] | |
| Izod notch impact strength | ASTM D256/ISO 179 | （28） kg·cm/cm(J/M)ft·lb/in | |
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | 25 % | |
| tensile yield strength | ASTM D-638 | 41 Mpa | |
| tensile elongation at break | ASTM D-638 | 25 % | |
| tensile breaking strength | ASTM D-638 | 32 Mpa | |
| Tensile yield elongation | ASTM D-638 | 2 % | |
| IZOD notch impact strength 73 ° F (23 ℃) | ASTM D-256 | 28 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238/ISO 1133 | 3.9 g/10min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ASTM D1525/ISO R306 | 92 ℃（℉） | |
| Vicat softening point (120 ℃/10hr) | ASTM D-1525 | 106 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.