Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Water absorption rate | 饱和,23°C,2.00mm | ISO62 | 1.4 | % |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO62 | 0.30 | % |
| Shrinkage rate | TD | ISO294-4 | 1.9 | % |
| Shrinkage rate | MD | ISO294-4 | 2.2 | % |
| MediumDensity | | | 1.19 | g/cm³ |
| SpecificHeatCapacity of Melt | | | 3000 | J/kg/°C |
| ThermalConductivityofMelt | | | 0.22 | W/m/K |
| Melt Volume-Flow Rate (MVR) | 190°C/2.16kg | ISO1133 | 2.20 | cm3/10min |
| Melt mass flow rate | | ISO1133 | 2.6 | g/10min |
| density | | ISO1183 | 1.42 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 14 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 15 | kJ/m² |
| Impact strength of cantilever beam gap | -40°C | ISO180/1A | 12 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 14 | kJ/m² |
| Poisson's ratio | | ISO527 | 0.35 | |
| TensileCreepModule | 1hr | ISO899-1 | 2700 | Mpa |
| Nominal tensile fracture strain | | ISO527-2 | 45 | % |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 400 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | NoBreak | |
| Tensile creep modulus | 1000hr | ISO899-1 | 1500 | Mpa |
| Tensile modulus | | ISO527-2 | 2950 | Mpa |
| tensile strength | 屈服 | ISO527-2 | 71.0 | Mpa |
| elongation | 屈服 | ISO527-2 | 25 | % |
| Rockwell hardness | M计秤 | ISO2039-2 | 88 | |
| Rockwell hardness | R计秤 | ISO2039-2 | 119 | |
| Bending modulus | | ISO178 | 2850 | Mpa |
| bending strength | 3.5%应变 | ISO178 | 77.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| vicat softening point | -- | ISO306/A50 | 175 | °C |
| vicat softening point | -- | ISO306/B50 | 160 | °C |
| Melting temperature | | ISO11357-3 | 178 | °C |
| Hot deformation temperature | 0.45MPa,未退火 | ISO75-2/B | 155 | °C |
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 95.0 | °C |
| Linear coefficient of thermal expansion | MD：-- | ISO11359-2 | 1.1E-04 | cm/cm/°C |
| Linear coefficient of thermal expansion | MD：-40to23°C | ISO11359-2 | 1E-04 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD：-- | ISO11359-2 | 1.1E-04 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD：-40to23°C | ISO11359-2 | 1E-04 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD：AnnealingTemperature | ISO11359-2 | 160 | °C |
| Linear coefficient of thermal expansion | TD：AnnealingTime-Optional | ISO11359-2 | 30.0 | min/mm |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Relative permittivity | 100Hz | IEC60250 | 3.90 | |
| Relative permittivity | 1MHz | IEC60250 | 3.90 | |
| Leakage Trace Index | | IEC60112 | 600 | V |
| Dielectric strength | | IEC60243-1 | 41 | KV/mm |
| Dissipation factor | 100Hz | IEC60250 | 3.5E-03 | |
| Dissipation factor | 1MHz | IEC60250 | 5.5E-03 | |
| Surface resistivity | | IEC60093 | 2E+13 | ohms |
| Volume resistivity | | IEC60093 | 1E+14 | ohms·cm |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.8mm | UL94 | HB | |
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| UL flame retardant rating | 0.8mm | IEC60695-11-10,-20 | HB | |
| UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | HB | |
| FMVSS flammability | | FMVSS302 | B | |
| Burning rate | 1.00mm | ISO3795 | 50 | mm/min |
| Fogging-F-value | refraction | ISO6452 | 91 | % |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|
| Emission | | VDA275 | <8.00 | mg/kg |
| EmissionofOrganicCompounds | | VDA277 | 4.70 | µgC/g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.