Technical Data Sheet
| 物理性能 | Test Condition | Test Method | Test Result |
|---|
| 收缩率 | 流动 : 2.00 mm | ASTM D955 | 0.30 % |
| 收缩率 | 横向流动 : 2.00 mm | ASTM D955 | 0.70 % |
| 吸水率 | 24 hr, 23°C | ASTM D570 | 0.20 % |
| 吸水率 | 24 hr, 100°C | ASTM D570 | 2.8 % |
| 热性能 | Test Condition | Test Method | Test Result |
|---|
| 载荷下热变形温度 | 1.8 MPa, 未退火 | ASTM D648 | 290 °C |
| 玻璃转化温度 | | DSC | 85.0 °C |
| 熔融温度 | | | 310 °C |
| 线性热膨胀系数 | 流动 | ASTM D696 | 2.5E-5 cm/cm/°C |
| 线性热膨胀系数 | 横向 | ASTM D696 | 5.5E-5 cm/cm/°C |
| 可燃性 | Test Condition | Test Method | Test Result |
|---|
| UL阻燃等级 | | UL 94 | V-0 |
| 机械性能 | Test Condition | Test Method | Test Result |
|---|
| 抗张强度 | | ASTM D638 | 160 Mpa |
| 伸长率 | 断裂 | ASTM D638 | 3.0 % |
| 弯曲模量 | | ASTM D790 | 14000 Mpa |
| 弯曲强度 | | ASTM D790 | 250 Mpa |
| 电气性能 | Test Condition | Test Method | Test Result |
|---|
| 体积电阻率 | | ASTM D257 | 1.0E+15 ohms·cm |
| 介电强度 | | ASTM D149 | 22 KV/mm |
| 介电常数 | 1 MHz | ASTM D150 | 4.30 |
| 耗散因数 | 1 MHz | ASTM D150 | 0.011 |
| 注射 | Test Condition | Test Method | Test Result |
|---|
| 干燥温度 | | | 110 °C |
| 干燥时间 | | | 2.0 到 6.0 hr |
| 料斗温度 | | | 50 到 90 °C |
| 料筒后部温度 | | | 300 到 325 °C |
| 料筒中部温度 | | | 315 到 335 °C |
| 料筒前部温度 | | | 320 到 335 °C |
| 射嘴温度 | | | 315 到 335 °C |
| 模具温度 | | | 90 到 140 °C |
| 注射速度 | | | 中等 |
| 螺杆转速 | | | 150 rpm |
| 硬度 | Test Condition | Test Method | Test Result |
|---|
| 洛氏硬度 | M 级 | ASTM D785 | 95 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.