PC FXD9810-WH7E217X SABIC INNOVATIVE NANSHA

Form：Granules | Grade：Flame retardant enhanced grade

Properties:

Low temperature resistancwear resistant

Typical Applications:

Home appliance componentsCast filmCasters

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Home appliance components \| Cast film \| Casters
Properties:	Low temperature resistanc \| wear resistant

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C, Total Energy	ASTM D3763	63.0	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.0 mm	UL 94	V-1
UL flame retardant rating	UL flame retardant rating	1.2 mm	UL 94	V-0
Burning wire flammability index	1.0 mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	1.0 mm	IEC 60695-2-13	875	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	Yield, 50.0 mm Span4	ASTM D790	94.0	Mpa
bending strength	bending strength	--5,6	ISO 178	91.0	Mpa
Bending modulus	--5	ISO 178	2250	Mpa
Bending modulus	Bending modulus	50.0 mm Span4	ASTM D790	2100	Mpa
elongation	Break	ISO 527-2/50	95	%
	elongation	Break3	ASTM D638	100	%
		elongation	Yield	ISO 527-2/50	5.6	%
		elongation	elongation	Yield3	ASTM D638	5.6	%
tensile strength	Break	ISO 527-2/50	49.0	Mpa
	tensile strength	Break3	ASTM D638	50.0	Mpa
		tensile strength	Yield	ISO 527-2/50	56.0	Mpa
		tensile strength	tensile strength	Yield3	ASTM D638	55.0	Mpa
Tensile modulus	--	ISO 527-2/1	2150	Mpa
Tensile modulus	Tensile modulus	--2	ASTM D638	2200	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			120	°C
drying time			3.0 to 4.0	hr
Suggested maximum moisture content			0.020	%
Suggested injection volume			40 to 60	%
Temperature at the rear of the barrel			250 to 270	°C
Temperature in the middle of the barrel			260 to 280	°C
Temperature at the front of the material cylinder			270 to 295	°C
Spray nozzle temperature			265 to 290	°C
Processing (melt) temperature			270 to 295	°C
Mold temperature			70 to 95	°C
Back pressure			0.300 to 0.700	Mpa
Screw speed			40 to 70	rpm
Exhaust hole depth			0.025 to 0.076	mm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	--	ISO 306/B120	138	°C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Vicat softening temperature	--	ISO 306/B50	137	°C
Vicat softening temperature	Vicat softening temperature	--	ASTM D15259	136	°C
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	118	°C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.1E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Flow : 23 to 80°C	ISO 11359-2	6.9E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	7.0E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 80°C	ISO 11359-2	6.8E-5	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.080	%
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	0.26	%
Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.40 - 0.80	%
Shrinkage rate	Shrinkage rate	Flow : 3.20 mm	Internal Method	0.40 - 0.80	%
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	29.0	cm3/10min
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	30	g/10 min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PC FXD9810-WH7E217X SABIC INNOVATIVE NANSHA

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index