PC/PET XYLEX™ X7300CL-GY8C088T SABIC INNOVATIVE US
101
- Properties:UV resistanceHigh mobility
- Usages:Automotive sector
Compare
View PricesTechnical Data Sheet
| 物理性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 熔体质量流动速率 | 265°C/2.16kg | ASTMD1238 | 21 g/10min |
| 熔体体积流动速率 | 265°C/2.16kg | ISO1133 | 21.0 cm3/10min |
| 收缩率 | MD：3.20mm | 内部方法 | 0.40to0.80 % |
| TD：3.20mm | 内部方法 | 0.50to0.70 % |
| 热性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 线性热膨胀系数 | TD：-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C |
| TD：23to60°C | ISO11359-2 | 8.5E-05 cm/cm/°C | |
| 热变形温度 | 0.45MPa,未退火,3.20mm | ASTMD648 | 102 °C |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 88.0 °C | |
| 热变形温度8 | 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 90.0 °C |
| 维卡软化温度 | ASTMD15259 | 108 °C | |
| ISO306/B120 | 106 °C | ||
| 线性热膨胀系数 | MD：-40到40°C | ASTME831 | 1.2E-04 cm/cm/°C |
| MD：23到60°C | ISO11359-2 | 8.5E-05 cm/cm/°C |
| 光学性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 透射率 | 2540µm | ASTMD1003 | 88.0 % |
| 雾度 | 2540µm | ASTMD1003 | 2.0 % |
| 机械性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 拉伸模量 | ASTMD638 | 1840 Mpa | |
| ISO527-2/1 | 1900 Mpa | ||
| 抗张强度 | 屈服 | ASTMD638 | 49.0 Mpa |
| 拉伸应力 | 屈服 | ISO527-2/50 | 55.0 Mpa |
| 抗张强度 | 断裂 | ASTMD638 | 52.0 Mpa |
| 拉伸应力 | 断裂 | ISO527-2/50 | 55.0 Mpa |
| 伸长率 | 屈服 | ASTMD638 | 5.0 % |
| 拉伸应变 | 屈服 | ISO527-2/50 | 5.0 % |
| 伸长率 | 断裂 | ASTMD638 | 150 % |
| 拉伸应变 | 断裂 | ISO527-2/50 | >150 % |
| 弯曲模量 | 50.0mm跨距 | ASTMD790 | 1940 Mpa |
| ISO178 | 2000 Mpa | ||
| 弯曲强度5,6 | ISO178 | 71.0 Mpa | |
| 弯曲强度 | 屈服,50.0mm跨距 | ASTMD790 | 83.0 Mpa |
| 冲击性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| NotchedIzodImpactStrength7 | 23°C | ISO180/1A | 9.0 kJ/m² |
| 装有测量仪表的落镖冲击 | 23°C,TotalEnergy | ASTMD3763 | 95.0 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.