| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.41 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 9.0 g/10min |
| Melt volume flow rate | | ISO 1133 | 8.00 cm3/10min |
| Water absorption rate | | ISO 62 | 0.50 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO 2039-2 | 80 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ColorNumber | | | CF2001/CF2001M |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527-2 | 62.0 Mpa |
| Nominal tensile fracture strain | | ISO 527-2 | 35 % |
| Flexural modulus | | ISO 178 | 2500 Mpa |
| bending strength | | ISO 178 | 87.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 6.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | IEC 60243-1 | 19 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 95.0 °C |
| Linear coefficient of thermal expansion | | 内部方法 | 1.2E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | | 内部方法 | 1.2E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.