Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.05 g/cm³ |
| Shrinkage rate | | | 1.1 % |
| Water absorption rate | | ISO 62 | 0.010 % |
| ash content | | ISO 3451 | 20 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 68 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ISO 527-2 | 27.0 MPa |
| tensile strength | Break | ISO 527-2 | 24.0 MPa |
| Tensile strain | Yield | ISO 527-2 | 3.0 % |
| Tensile strain | Break | ISO 527-2 | 2.9 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180/A | 16 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | | 165 °C |
| Heat distortion temperature | | ISO 75-2/Be | 130 °C |
| vicat | | ISO 306/B120 | 150 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare