PA6 B1S25 G25
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.33 g/cm³ | |
| ISO 1183/A | 1.33 g/cm³ | ||
| Humidity | ISO 15512/B | <0.25 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 8300 MPa | |
| Charpy Notched Impact Strength | ISO 179/1eA | 10 kJ/m² | |
| ISO 179/1eU | 60 kJ/m² | ||
| Flexural modulus | ISO 178 | 6200 MPa | |
| bending strength | ISO 178 | 205 MPa | |
| Tensile modulus | ISO 527-2 | 8300 MPa | |
| tensile strength | Break | ISO 527-2/5 | 160 MPa |
| Tensile strain | Yield | ISO 527-2/5 | 3.5 % |
| Flexural modulus | ISO 178 | 6200 MPa | |
| bending strength | ISO 178 | 205 MPa | |
| tensile strength | Break | ISO 527-2 | 160 MPa |
| Tensile strain | Break | ISO 527-2 | 3.5 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 10 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179/1eU | 60 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature (HDT) | ISO 75-2/A | 200 °C | |
| vicat | ISO 306 | > 200 °C | |
| Hot deformation temperature (HDT) | ISO 75-2/A | 200 °C | |
| vicat | ISO 306/B | >200 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.