PP MAJ'ECO FP374HGB
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | 内部方法 | 0.80to1.1 % | |
| density | ISO1183 | 1.07 g/cm³ | |
| melt mass-flow rate | ISO1133 | 7.0 g/10min | |
| ISO1133 | 20 g/10min | ||
| ISO1133 | 7.0 g/10min | ||
| ISO1133 | 20 g/10min | ||
| Shrinkage rate | 内部方法 | 0.80to1.1 % | |
| density | ISO1183 | 1.07 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL94 | HB | |
| UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO527-2/1 | 4700 MPa | |
| Tensile stress | Yield | ISO527-2/50 | 50.0 MPa |
| Flexural modulus | ISO178 | 4350 MPa | |
| Bending stress | ISO178 | 88.0 MPa | |
| Tensile modulus | ISO527-2/1 | 4700 MPa | |
| Tensile stress | Yield | ISO527-2/50 | 50.0 MPa |
| Flexural modulus | ISO178 | 4350 MPa | |
| Bending stress | ISO178 | 88.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO179/1eA | 8.6 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO179/1eU | 23 kJ/m² | |
| Charpy Notched Impact Strength | ISO179/1eA | 8.6 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO179/1eU | 23 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.