Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.09 g/cm³ |
| Water absorption rate | | ASTMD570 | 0.19 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 67 |
| Barcol Hardness | | ASTMD2583 | 54 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Gardner glossiness | | ASTMD523 | 87 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| HotFormingTemperature | | 内部方法 | 149到171 °C |
| HotFormingTemperature | | 内部方法 | 177到193 °C |
| HotFormingTemperature | | 内部方法 | None |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTMD638 | 2550 MPa |
| tensile strength | | ASTMD638 | 45.5 MPa |
| elongation | | ASTMD638 | 4.4 % |
| Flexural modulus | | ASTMD790 | 2340 MPa |
| Flexural modulus | | ASTMD790 | 2250 MPa |
| bending strength | | ASTMD790 | 62.7 MPa |
| bending strength | | ASTMD790 | 74.5 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256A | 110 J/m |
| Dart impact equipped with measuring instruments | | 内部方法 | 16.7 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 85.6 °C |
| | ASTMD696 | 8.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.