Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | 内部方法 | 0.50to0.80 % |
| melt viscosity | | ASTMD3835 | 225 Pa·s |
| melt mass-flow rate | | ASTMD1238 | 5.6 g/10min |
| melt mass-flow rate | | ISO1133 | 18 g/10min |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTMD638 | 2280 Mpa |
| tensile strength | | ASTMD638 | 44.0 Mpa |
| tensile strength | | ASTMD638 | 34.0 Mpa |
| elongation | | ASTMD638 | 2.0 % |
| elongation | | ASTMD638 | 24 % |
| Flexural modulus | | ASTMD790 | 2340 Mpa |
| bending strength | | ASTMD790 | 72.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Dart impact equipped with measuring instruments | | ASTMD3763 | 31.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Arc resistance 6 | | ASTMD495 | PLC6 |
| Compared to the Leakage Tracking Index (CTI) | | UL746 | PLC 0 |
| High arc combustion index (HAI) | | UL746 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | | UL746 | PLC 3 |
| Hot wire ignition (HWI) | | UL746 | PLC 3 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 94.0 °C |
| | ASTMD648 | 80.0 °C |
| vicat | | ASTMD15255 | 99.0 °C |
| | ASTME831 | 8.8E-05 cm/cm/°C |
| | ASTME831 | 8.8E-05 cm/cm/°C |
| RTI Elec | | UL746 | 60.0 °C |
| RTI Imp | | UL746 | 60.0 °C |
| RTI Str | | UL746 | 60.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.