PPO HS2000X-80267 SABIC INNOVATIVE SINGAPHORE

Form：Granules | Grade：Injection grade

Properties:

Glass fiber mineral reinf

Typical Applications:

medical care

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	medical care
Properties:	Glass fiber mineral reinf

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
23°C		ASTM D256	130	J/m
23°C	23°C		ISO 180/1A	9.7	kJ/m²
Suspended wall beam without notch impact strength	23°C	ASTM D4812	2200	J/m
Reverse notch impact	3.20mm	ASTM D256	810	J/m
Dart impact	23°C,TotalEnergy	ASTM D3763	443	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.47mm	UL 94	V-0
	UL flame retardant rating	2.01mm	UL 94	5VA
	UL flame retardant rating	UL flame retardant rating	RadiantPanelListing(UL)	UL 94	YES
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
--1		ASTM D638	3650	Mpa
yield		ASTM D638	74.0	Mpa
Yield, 100mm span		ASTM D790	117	Mpa
Fracture, 50.0mm span		ASTM D790	117	Mpa
yield		ISO 527-2	71.7	Mpa
crack		ASTM D638	60.0	Mpa
crack	crack		ISO 527-2	57.1	Mpa
yield		ASTM D638	3.8	%
yield	yield		ISO 527-2	3.7	%
crack		ASTM D638	8.4	%
crack	crack		ISO 527-2	11	%
100mm span 5	100mm	ASTM D790	3550	Mpa
50.0mm span		ASTM D790	3670	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
0.45MPa, unannealed, 6.40mm		ASTM D648	128	°C
0.45MPa, unannealed, 100mm span		ISO 75-2/Be	126	°C
1.8MPa, unannealed, 3.20mm		ASTM D648	108	°C
1.8MPa, unannealed, 6.40mm		ASTM D648	116	°C
1.8MPa, unannealed, 100mm span		ISO 75-2/Ae	111	°C
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	7.1E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	7.8E-05	cm/cm/°C
RTI Elec		UL 746	100	°C
0.45MPa, unannealed, 3.20mm		ASTM D648	117	°C
RTI Imp		UL 746	85.0	°C
RTI		UL 746	100	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	280°C/5.0kg	ASTM D1238	7.6	g/10min
melt mass-flow rate	melt mass-flow rate	300°C/5.0kg	ASTM D1238	7.6	g/10min
Melt Volume Flow Rate (MVR)	280°C/5.0kg	ISO 1133	6.80	cm3/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR)	300°C/5.0kg	ISO 1133	6.80	cm3/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70	%
Outdoor applicability		UL 746C	f1
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	1MHz	ASTM D150	4.4E-03
Arc resistance		ASTM D495	PLC6
Compared to the anti leakage trace index	CTI	UL 746	PLC 2
High arc combustion index	HAI	UL 746	PLC 2
High voltage arc tracing rate	HVTR	UL 746	PLC 3
Hot wire ignition	HWI	UL 746	PLC 0
Surface resistivity		ASTM D257	>1.0E+16	ohms
Volume resistivity		ASTM D257	1.2E+16	ohms·cm
Dielectric strength	3.20mm,inOil	ASTM D149	17	KV/mm
Dielectric constant	50Hz	ASTM D150	2.89
	Dielectric constant	60Hz	ASTM D150	2.89
	Dielectric constant	Dielectric constant	1MHz	ASTM D150	2.70
Dissipation factor	50Hz	ASTM D150	0.017
Dissipation factor	Dissipation factor	60Hz	ASTM D150	0.017

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.