Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 294-4 | 1.2 % |
| Shrinkage rate | | ISO 294-4 | 0.30 % |
| Water absorption rate | | ISO 62 | 1.6 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | IEC 60695-11-10, -20 | V-0 |
| Flammability level | | IEC 60695-11-10, -20 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 12000 Mpa |
| Tensile modulus | | ISO 527-2 | 8000 Mpa |
| Tensile modulus | | ISO 527-2 | 5500 Mpa |
| Tensile stress | | ISO 527-2 | 155 Mpa |
| Tensile stress | | ISO 527-2 | 105 Mpa |
| Tensile stress | | ISO 527-2 | 70.0 Mpa |
| Tensile strain | | ISO 527-2 | 2.0 % |
| Tensile strain | | ISO 527-2 | 2.7 % |
| Tensile strain | | ISO 527-2 | 3.7 % |
| Flexural modulus | | ISO 178 | 11500 Mpa |
| Bending stress | | ISO 178 | 245 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 50 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | IEC 60243-1 | 33 KV/mm |
| | IEC 60250 | 4.20 |
| | IEC 60250 | 3.90 |
| | IEC 60250 | 3.90 |
| | IEC 60250 | 3.90 |
| CTI | | IEC 60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO 75-2/A | 305 °C |
| Melting temperature 3 | | ISO 11357-3 | 325 °C |
| | ASTM D696 | 3.0E-5 cm/cm/°C |
| | ASTM D696 | 3.5E-5 cm/cm/°C |
| RTI Elec | | UL 746 | 140 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.