PC/PBT X2420 BK1066 SABIC INNOVATIVE NANSHA

Form：Granules | Grade：Chemical resistance

Properties:

High mobilityHigh impact resistanceDimensional stabilityFiller: Glass fiber reinf10% filler by weight

Typical Applications:

Automotive Applications

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive Applications
Properties:	High mobility \| High impact resistance \| Dimensional stability \| Filler: Glass fiber reinf \| 10% filler by weight

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179/1eA	15	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	7.0	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	95	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	95	kJ/m²
23°C		ASTM D256	210	J/m
-30°C		ISO 180/1A	8.0	kJ/m²
23°C		ISO 180/1A	14	kJ/m²
23°C	23°C		ASTM D4812	1600	J/m
-30°C		ISO 180/1U	74	kJ/m²
23°C		ISO 180/1U	110	kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	36.0	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.400mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	Yield,50.0mmSpan	ASTM D790	90.0	Mpa
Bending modulus	50.0mmSpan	ASTM D790	3500	Mpa
crack		ISO 527-2/5	7.0	%
yield		ISO 527-2/5	3.0	%
yield	yield		ASTM D638	3.0	%
crack		ISO 527-2/5	37.0	Mpa
crack	crack		ASTM D638	35.0	Mpa
yield		ISO 527-2/5	51.0	Mpa
yield	yield		ASTM D638	50.0	Mpa
Tensile modulus		ASTM D638	3800	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI Elec		UL 746	75.0	°C
RTI Imp		UL 746	75.0	°C
RTI		UL 746	75.0	°C
Horizontal: 23 to 80 ° C	Across Flow, 23to80℃	ISO 11359-2	9E-05	cm/cm/°C
Horizontal: -40 to 40 ° C	Across Flow, -40to40℃	ASTME831	8E-05	cm/cm/°C
Flow: 23 to 80 ° C	23to80℃	ISO 11359-2	4E-05	cm/cm/°C
Flow: -40 to 40 ° C		ASTME831	5E-05	cm/cm/°C
Vicat softening temperature		ISO 306/B120	118	°C
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	101	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	111	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.040	%
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.020	%
Shrinkage rate	TD:3.20mm	Internal Method	0.30-0.40	%
Shrinkage rate	Shrinkage rate	MD:3.20mm	Internal Method	0.15-0.25	%
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	26.0	cm3/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR)	265°C/2.16kg	ISO 1133	12.0	cm3/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.