Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Full light transmittance coefficient | | ASTM D-1003 | MF｜93 % |
| Full light transmittance coefficient | | ASTM D-1003 | V｜93 % |
| refractive index | | ASTM D-542 | MF｜1.49 |
| refractive index | | ASTM D-542 | V｜1.49 |
| processability | Test Condition | Test Method | Test Result |
|---|
| Forming shrinkage rate | | ASTM D-955 | MF｜0.2-0.6 % |
| Forming shrinkage rate | | ASTM D-955 | V｜0.2-0.6 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ASTM D-570 | MF｜0.3 % |
| Water absorption rate | | ASTM D-570 | V｜0.3 % |
| melt mass-flow rate | | ASTM D-1238 | MF｜2.0 g/10min |
| melt mass-flow rate | | ASTM D-1238 | V｜2.5 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D-785 | MF｜100 M Scale |
| Rockwell hardness | | ASTM D-785 | V｜95 M Scale |
| | ASTM D-638 | MF｜5 % |
| | ASTM D-638 | V｜5 % |
| Izod impact strength | | ASTM D-255 | MF｜1.7 kg·cm/cm |
| Izod impact strength | | ASTM D-255 | V｜1.6 kg·cm/cm |
| tensile strength | | ASTM D-638 | MF｜740 kg/cm2 |
| tensile strength | | ASTM D-638 | V｜730 kg/cm2 |
| compressive strength | | ASTM D-695 | MF｜1100 kg/cm2 |
| compressive strength | | ASTM D-695 | V｜1100 kg/cm2 |
| | ASTM D-790 | MF｜3.2×104 kg/cm2 |
| | ASTM D-790 | V｜3.1×104 kg/cm2 |
| bending strength | | ASTM D-790 | MF｜1100 kg/cm2 |
| bending strength | | ASTM D-790 | V｜1100 kg/cm2 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | | V｜3.7 |
| Surface Resistivity | | JIS K-6911 | MF｜>1016 |
| Surface Resistivity | | JIS K-6911 | V｜>1016 |
| dielectric loss tangent | | | MF｜0.05 |
| dielectric loss tangent | | | V｜0.05 |
| volume resistivity | | JIS K-6911 | MF｜>1015 |
| volume resistivity | | JIS K-6911 | V｜>1015 |
| arc resistance | | JIS K-6911 | MF｜没有痕迹 |
| arc resistance | | JIS K-6911 | V｜没有痕迹 |
| Insulation breakdown strength | | | MF｜20 |
| Insulation breakdown strength | | | V｜20 |
| dielectric constant | | | MF｜3.7 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ASTM D-1525 | MF｜116 °C |
| vicat | | ASTM D-1525 | V｜107 °C |
| | ASTM C-177 | MF｜5×10-4 Cal/s/cm/℃ |
| | ASTM C-177 | V｜5×10-4 Cal/s/cm/℃ |
| specific heat | | | MF｜0.35 cal/g/℃ |
| specific heat | | | V｜0.35 cal/g/℃ |
| linear expansion coefficient | | ASTM D-696 | MF｜6×10-5 cm/cm/℃ |
| linear expansion coefficient | | ASTM D-696 | V｜6×10-5 cm/cm/℃ |
| Load deflection temperature | | ASTM D-648 | MF｜102 °C |
| Load deflection temperature | | ASTM D-648 | V｜92 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.