Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 15 g/10min |
| density | | ISO 1183 | 1.40 g/cm³ |
| density | | ASTM D792 | 1.40 g/cm³ |
| Shrinkage rate | | ISO 2577 | 0.30to0.50 % |
| Shrinkage rate | | ASTM D955 | 0.30to0.50 % |
| melt mass-flow rate | | ISO 1133 | 15 g/10min |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Burning wire flammability index | | IEC 60695-2-12 | 850 °C |
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO 178 | 6800 MPa |
| bending strength | | ASTM D790 | 120 MPa |
| Flexural modulus | | ASTM D790 | 6800 MPa |
| Tensile strain | Break | ISO 527-2 | 2.5 % |
| elongation | Break | ASTM D638 | 2.5 % |
| tensile strength | Yield | ISO 527-2 | 100 MPa |
| tensile strength | Yield | ASTM D638 | 100 MPa |
| bending strength | | ISO 178 | 120 MPa |
| Tensile modulus | | ISO 527-2 | 6600 MPa |
| Tensile modulus | | ASTM D638 | 6600 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180 | 8.0 kJ/m² |
| Impact strength of cantilever beam gap | | ASTM D256 | 100 J/m |
| Impact strength of cantilever beam gap | | ISO 180 | 10 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | IEC 60250 | 3.50 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 135 °C |
| Heat distortion temperature | | ASTM D648 | 135 °C |
| Heat distortion temperature | | ISO 75-2/B | 195 °C |
| Heat distortion temperature | | ASTM D648 | 195 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.