Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO62 | 0.60 % |
| Water absorption rate | | ISO62 | 0.70 % |
| Water absorption rate | | ISO62 | 0.20 % |
| MediumDensity | | | 1.02 g/cm³ |
| density | | ISO1183 | 1.16 g/cm³ |
| melt mass-flow rate | | ISO1133 | 5.6 g/10min |
| Melt volume flow rate | | ISO1133 | 5.00 cm³/10min |
| Shrinkage rate | | ISO294-4 | 0.40 % |
| Shrinkage rate | | ISO294-4 | 0.20 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO868 | 43 |
| | ISO868 | 37 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | ISO4589-2 | 20 % |
| FMVSS flammability | | FMVSS302 | SE |
| UL flame retardant rating | | UL94 | HB |
| Flammability level | | IEC60695-11-10,-20 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ISO527-2 | 2.40 MPa |
| Tensile stress | | ISO527-2 | 4.60 MPa |
| Tensile stress | | ISO527-2 | 8.40 MPa |
| Tensile strain | Break | ISO527-2 | >300 % |
| Nominal tensile fracture strain | | ISO527-2 | 500 % |
| Tensile modulus | | ISO527-2 | 60.0 MPa |
| Tensile stress | Break | ISO527-2 | 26.0 MPa |
| Tensile creep modulus | | ISO899-1 | 40.0 MPa |
| Flexural modulus | | ISO178 | 60.0 MPa |
| abrasion resistance | | ISO4649 | 200 mm³ |
| TensileCreepModule | | ISO899-1 | 54.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | NoBreak |
| Impact strength of simply supported beam without notch | | ISO179/1eU | NoBreak |
| Impact strength of simply supported beam without notch | | ISO179/1eU | NoBreak |
| Impact strength of cantilever beam gap | | ISO180/1A | NoBreak |
| Impact strength of cantilever beam gap | | ISO180/1A | NoBreak |
| Tensile impact strength | | ISO8256/1 | 230 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | NoBreak |
| Charpy Notched Impact Strength | | ISO179/1eA | NoBreak |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tear strength | Across Flow | ISO34-1 | 96 kN/m |
| tear strength | | ISO34-1 | 100 kN/m |
| film | Test Condition | Test Method | Test Result |
|---|
| Water vapor permeability | | DIS15106-1/-2 | 450 g/m²/24hr |
| OxygenTransmissionRate | | DIS15105-1/-2 | 14000 cm³/m²/bar/24hr |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| | IEC60250 | 5.20 |
| Surface Resistivity | | IEC60093 | 2E+14 ohms |
| Volume resistivity | | IEC60093 | 7E+12 ohms·cm |
| dielectric strength | | IEC60243-1 | 18 kV/mm |
| | IEC60250 | 4.70 |
| Dissipation Factor | | IEC60250 | 0.011 |
| Dissipation Factor | | IEC60250 | 0.053 |
| CTI | | IEC60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO11359-2 | 1.6E-04 cm/cm/°C |
| EffectiveThermal Diffusivity | | | 8.5E-08 m²/s |
| brittle temperature | | ISO974 | -97.0 °C |
| Glass Transition Temperature | | ISO11357-2 | -50.0 °C |
| melting temperature | | ISO11357-3 | 152 °C |
| | ISO11359-2 | 1.3E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.