PA66 2703T
11
- Properties:TougheningHigh impact resistanceLow temperature resistancHigh modulus tougheningLow temperature resistancHigh impact resistance
- Usages:Industrial applicationssporting goodsBottle capPA pipeUsed for railway fender seatPipe fittingsSports equipment
CompareTechnical Data Sheet
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | -- g/cm | |
| Shrinkage rate | - | 1.00 % | |
| - | 1.25 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | 61.3 KJ/m | |
| Impact strength of cantilever beam gap | ISO 180 | 63.3 KJ/m | |
| elongation at break | ISO 527 | 26.47 % | |
| Charpy Notched Impact Strength | ISO 179 | 不断 KJ/m | |
| tensile strength | ISO 527 | 53.11 Mpa | |
| Tensile modulus | ISO 527 | 1.86 GPa | |
| Flexural modulus | ISO 178 | 1.14 GPa | |
| bending strength | ISO 178 | 47.97 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | IEC 93 | -- Ω.cm | |
| dielectric strength | IEC 243 | -- KV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | ISO 3146 | 253-257 °C | |
| Linear coefficient of thermal expansion | ISO 11359 | 80 | |
| melt mass-flow rate | ISO 1133 | 47.2 g/10min | |
| Heat distortion temperature | ISO 75 | 73.1 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.