Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO294-4 | 1.1 % |
| Shrinkage rate | | ISO294-4 | 1.1 % |
| Ash Content | | ISO3451 | 28 % |
| melt mass-flow rate | | ISO1133 | 20 g/10min |
| density | | ISO1183 | 1.10 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO868 | 72 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ISO527-2/20 | 25.0 MPa |
| Tensile stress | | ISO527-2/20 | 20.0 MPa |
| Tensile strain | | ISO527-2/20 | 8.0 % |
| Tensile strain | | ISO527-2/20 | 50 % |
| Flexural modulus | | ISO178 | 2200 MPa |
| Bending stress | | ISO178 | 36.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179/1eU | 45 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 2.5 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 4.5 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 60.0 °C |
| vicat | | ISO306/B50 | 83.0 °C |
| BallPressure Test | | IEC335 | 通过 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.