Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Apparent density | | g/cm³ | 0.52to0.53 |
| Melt volume flow rate | | cm³/10min | 0.01to0.25 |
| spiral flow length | | mm | 500.38to800.10 |
| flow | | mm/mm | 0.330to0.457 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | | 75to98 |
| Rockwell hardness | | | 58to68 |
| ball-indentation hardness | | | 44.83to60.0 Mpa |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | | 79to132 |
| Haze ratio | | % | 0.40to17 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | kJ/m² | 1.114to45.037 |
| Suspended wall beam without notch impact strength | | J/m | 0.013to0.024 |
| Dart impact | | N.m | 1831.86to2831.86 |
| Charpy Notched Impact Strength | | kJ/m² | 0.651to5.107 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| yield | | % | 6.0to28 |
| yield | | | 19.59to31.38 Mpa |
| Tensile modulus | | | 0.15to1.0 |
| yield | | | 24.41to30.48 Mpa |
| fracture | | % | 78to510 |
| fracture | | | 19.31to44.34 Mpa |
| yield | | % | 10to16 |
| Flexural modulus | | | 737.93to827.59 Mpa |
| fracture | | % | 46to510 |
| bending strength | | | 6.5to25.03 Mpa |
| fracture | | | 14.48to40.0 Mpa |
| film | Test Condition | Test Method | Test Result |
|---|
| MD | | | 344.83to793.1 Mpa |
| film thickness | | mil | 2.0to3.1 |
| fracture | | % | 500to760 |
| fracture | | | 29.03to39.59 Mpa |
| MD: Fracture | | | 20.34to40.55 Mpa |
| MD: Fracture | | % | 490to760 |
| Dart impact | | J | 0.54to16.45 |
| Initial sealing temperature | | °C | 105to115 |
| MD: Surrender | | | 18.0to22.62 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.